ROOFCOAT
(Ready-to-use Silicone Roof Coating)

PRODUCT DESCRIPTION

ROOFCOAT is a ready-to-use, one part elastomeric coating for water proofing and UV protection, with a paintable consistency that cures to a skin on exposure to atmospheric moisture.  Moreover the finished coating is vapour permeable allowing interior condensation to escape while preventing exterior moisture, rain etc., from entering.    Because of this feature the surface is not subject to blistering and cracking.

KEY PERFORMANCE PROPERTIES

  • Single component, ready-to-use
  • Easy application by brush, roller or spray
  • Excellent adhesion to concrete, wood and other porous roofs
  • Excellent UV resistance
  • Durable and flexible at temperature range -50 degree C to +100 degree C
  • Good resistance to acidic and alkaline environments   
TYPICAL PRODUCT DATA

Uncured Properties

Cured Properties

 

Cure System                                                   Tack Free Time

Full Cure

Colour

Specific gravity

Flash Point, 0 degree C

 

Neutral

90 mins

1-2 days

White

0.91

32

 

Tensile Strength

Elongation

 

1.5 MPa

450%

INSTRUCTION FOR USE

ROOFCOAT can be applied to almost all types of roofs: concrete, wood, and fiber cement etc.  The system is not recommended over bituminous surfaces.

SILCOAT FC (Fast Cure Silicon Roof Coating)

PRODUCT DESCRIPTION

SILCOAT FC is an improved, one part elastomeric coating for water proofing and UV protection, with a paintable consistency that cures to a skin on exposure to atmospheric moisture.  Moreover the finished coating is vapour permeable allowing interior condensation to escape while preventing exterior moisture, rain etc., from entering.    Because of this feature the surface is not subject to blistering and cracking.

KEY PERFORMANCE PROPERTIES

  • Fast curing and easy application
  • Low maintenance cost
  • Durability - resists UV attack and will not harden or crack
  • Protects interior finishes
  • Provides resistance from harsh acidic and alkaline environments
  • Good performance over wide temperature range -50 degree C to + 100 degree C
TYPICAL PRODUCT DATA

Uncured Properties

Cured Properties

 

Cure System                                                    Tack Free Time

Full Cure

Colour

Specific gravity

Flash Point, 0 degree C

 

Neutral

90 mins

1-2 days

White

0.96

32

 

Tensile Strength

Elongation

 

1.5 MPa

450%

METHOD OF APPLICATION

Stir ROOFCOAT mixture well just before application . Two coats are required to achieve a film thickness of 100 microns (0.1mm) or more . Apply the first coat on naked roof immediately after surface preparation . The second coat has to be applied after 6 to 8 hours , from the time of applying the first coat , depending on temperature and humidity . The coverage is around 20 sq.ft/litre .

INSTRUCTION FOR USE

SILCOAT can be applied to almost all types of roofs: concrete, wood, and fiber cement etc.  The system is not recommended over bituminous surfaces.